Gap filling of shallow trench isolation by ozone-tetraethoxysilane

ABSTRACT

A method for filling a trench within a silicon substrate. There is first provided a silicon substrate having a trench formed therein. There is then oxidized thermally the silicon substrate to form within the trench a thermal silicon oxide trench liner layer. There is then treated the thermal silicon oxide trench liner layer by exposure to a plasma formed from a gas composition which upon plasma activation simultaneously supplies an active nitrogen containing species and an active oxygen containing species to form a plasma treated thermal silicon oxide trench liner layer. There is then formed upon the plasma treated thermal silicon oxide trench liner layer a conformal silicon oxide intermediate layer formed through a plasma enhanced chemical vapor deposition (PECVD) method employing a silane silicon source material. Finally, there is then formed upon the conformal silicon oxide intermediate layer a gap filling silicon oxide trench fill layer through an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employing an ozone oxidant and a tetra-ethyl-ortho-silicate (TEOS) silicon source material.

CROSS-REFERENCE TO RELATED APPLICATION

This application is related to co-assigned and co-invented application Ser. No. 08/873,836 filed Jun. 12, 1997, now U.S. Pat. No. 5,741,740.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates generally to methods for forming trench fill layers within trenches within substrates employed in microelectronics fabrication. More particularly, the present invention relates to methods for forming gap filling trench fill layers within trenches within substrates employed in microelectronics fabrication.

2. Description of the Related Art

Integrated circuits are formed from semiconductor substrates within and upon whose surfaces are formed resistors, transistors, diodes, and other electrical circuit elements. The electrical circuit elements are connected internally and externally to the semiconductor substrate upon which they are formed through patterned conductor layers which are separated by dielectric layers.

As integrated circuit device technology has advanced and integrated circuit device dimensions have decreased, it has become increasingly common within advanced integrated circuits to employ trench isolation methods such as shallow trench isolation (STI) methods and recessed oxide isolation (ROI) methods to form trench isolation regions nominally co-planar with adjoining active semiconductor regions of semiconductor substrates. Such trench isolation methods typically employ a chemical mechanical polish (CMP) planarizing method to provide a nominally planarized surface to a trench isolation region formed from a trench fill dielectric layer formed within the trench. Trench isolation regions nominally co-planar with active semiconductor regions within semiconductor substrates are desirable since they optimize, when subsequently forming patterned layers upon those nominally co-planar regions, the limited depth of focus typically achievable with advanced photoexposure tooling.

When forming within advanced integrated circuits trench isolation regions within isolation trenches, it has become common to employ as trench fill dielectric layers gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods. Silicon oxide layers formed employing such methods are desirable since such silicon oxide layers typically possess the inherently superior gap filling characteristics desirable for trenches of limited dimensions typically encountered in advanced integrated circuit fabrication.

While gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods are thus desirable as trench fill layers within trenches within advanced integrated circuit fabrication, methods through which are formed such gap filling silicon oxide layers are not entirely without problems. Specifically, it is known in the art of integrated circuit fabrication that gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods exhibit a surface sensitivity dependent upon the substrate layers upon which are formed those gap filling silicon oxide layers. In particular, when employing as substrate layers thermally grown silicon oxide layers which are typically employed as isolation trench liner layers within isolation trenches formed within silicon semiconductor substrates, gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods exhibit inhibited formation rates in comparison with otherwise equivalent gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods upon substrate layers other than thermally grown silicon oxide layers. The gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods upon the thermally grown silicon oxide layers also typically exhibit inferior bulk quality (as determined by wet etch rates in dilute hydrofluoric acid) and enhanced surface roughness in comparison with otherwise equivalent gap filling silicon oxide layers formed employing ozone assisted sub-atmospheric thermal chemical vapor deposition (SACVD) methods upon substrate layers other than thermally grown silicon oxide layers. Inhibited formation rates within isolation trenches within semiconductor substrates of gap filling silicon oxide trench fill layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods are undesirable since there is then formed within those isolation trenches gap filling silicon oxide layers which are particularly susceptible to dishing when subsequently planarized employing chemical mechanical polish (CMP) planarizing methods. Similarly, inferior bulk quality of such gap filling silicon oxide trench fill layers is undesirable since inferior bulk quality of such gap filling silicon oxide trench fill layers often compromises the dielectric properties of such gap filling silicon oxide trench fill layers. Finally, enhanced surface roughness of such gap filling silicon oxide trench fill layers is undesirable since enhanced surface roughness of such gap filling silicon oxide trench fill layers often provides gap filling silicon trench fill layers of enhanced porosity.

It is thus towards the goal of forming within advanced integrated circuits gap filling silicon oxide trench fill layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods with enhanced bulk quality and diminished surface roughness, while attenuating a surface sensitivity when forming those gap filling silicon oxide trench fill layers, that the present invention is generally directed.

Methods and materials through which silicon oxide layers may be formed with desirable properties within integrated circuits are known in the art of integrated circuit fabrication. For example, Jang et al., in U.S. Pat. No. 5,536,681, disclose a method for improving the gap filling capabilities of silicon oxide layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods. The method employs a nitrogen plasma treatment upon selected topographic portions of a silicon oxide substrate layer formed employing a plasma enhanced chemical vapor deposition (PECVD) method, upon which silicon oxide substrate layer is formed a gap filling oxide layer formed employing an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method.

Further, Jang et al., in U.S. Pat. No. 5,726,090, disclose a method for enhancing gap filling characteristics of ozone assisted sub-atmospheric pressure thermal chemical vapor deposited (SACVD) silicon oxide dielectric layers formed upon thermal silicon oxide trench liner layers within semiconductor substrates within semiconductor integrated circuit microelectronics fabrications. The method employs an intermediate silicon oxide trench liner layer formed upon the thermal silicon oxide trench liner layer prior to forming the ozone assisted sub-atmospheric pressure thermal chemical vapor deposited (SACVD) silicon oxide dielectric layer over the thermal silicon oxide trench liner layer, where the intermediate silicon oxide trench liner layer is treated with a nitrogen plasma prior to forming the ozone assisted sub-atmospheric pressure thermal chemical vapor deposited (SACVD) silicon oxide dielectric layer thereupon.

Finally, Jang et al., in U.S. Pat. No. 5,731,241, disclose a method for protecting a trench fill silicon oxide layer from excessive etching during multiple etching steps. The method employs forming a conformal silicon oxide layer employing sub-atmospheric pressure chemical vapor deposition (SACVD) upon a silicon oxide trench fill layer within a trench within a silicon substrate, wherein the conformal silicon oxide layer has a greater differential etch rate over the trench fill region and functions as a sacrificial layer to protect the trench fill silicon oxide.

Desirable in the art are additional methods through which trenches within substrates employed within integrated circuit fabrication may be filled with gap filling silicon oxide trench fill layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods, while: (1) attenuating a surface sensitivity when forming those gap filling silicon oxide trench fill layers; (2) providing gap filling silicon oxide trench fill layers with enhanced bulk quality (as determined, for example, employing etch rates in dilute hydrofluoric acid); and (3) providing gap filling silicon oxide trench fill layers with diminished surface roughness. Particularly desirable in the art are additional methods through which isolation trenches within semiconductor substrates employed within integrated circuit fabrication may be filled with gap filling silicon oxide trench fill dielectric layers formed employing ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods upon thermal silicon oxide trench liner layers within isolation trenches within silicon semiconductor substrates within semiconductor integrated circuits within microelectronics fabrications in accord with the foregoing three objects. It is towards these goals that the present invention is generally and more specifically directed.

SUMMARY OF THE INVENTION

A first object of the present invention is to provide a method through which a trench within a substrate employed in microelectronics fabrication may be filled with a gap filling silicon oxide trench fill layer formed employing a sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method

A second object of the present invention is to provide a method in accord with the first object of the present invention, where there is attenuated a surface sensitivity when forming the silicon oxide trench fill layer upon a thermal silicon oxide trench liner layer.

A third object of the present invention is to provide a method in accord with the first object of the present invention, where there is provided the gap filling silicon oxide trench fill layer with enhanced bulk quality (as determined employing etch rate in dilute hydrofluoric acid).

A fourth object of the present invention is to provide a method in accord with the first object of the present invention, where there is provided the gap filling silicon oxide trench fill layer with diminished surface roughness.

A fifth object of the present invention is to provide a method in accord with the second object of the present invention, the third object of the present invention and/or the fourth object of the present invention, where the substrate is a semiconductor substrate and the trench is an isolation trench within the semiconductor substrate.

A sixth object of the present invention is to provide a method, in accord with the first object of the present invention, the second object of the present invention, the third object of the present invention, the fourth object of the present invention, and/or the fifth object of the present invention, which method is readily commercially implemented.

In accord with the objects of the present invention, there is provided by the present invention a method for forming within a trench within a substrate employed in microelectronics fabrication a gap filling silicon oxide trench fill layer. To practice the method of the present invention, there is first provided a silicon substrate having a trench formed therein. There is then thermally oxidized the silicon substrate to form within the trench a thermal silicon oxide trench liner layer. There is then provided a plasma formed from a gas or gases which upon plasma activation provides simultaneously active nitrogen-containing species and active oxygen-containing species to which the thermal silicon oxide trench liner layer surface is exposed. There is then formed upon the plasma treated thermal silicon oxide trench liner layer a conformal silicon oxide intermediate layer formed through a plasma enhanced chemical vapor deposition (PECVD) method employing a silane silicon source material. Finally, there is formed upon the conformal silicon oxide intermediate layer a gap filling silicon oxide trench fill layer formed through an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employing an ozone oxidant and a tetra-ethyl-ortho-silicate (TEOS) silicon source material.

The present invention provides a method through which there may be formed within a trench within a substrate employed in integrated circuit fabrication a gap filling silicon oxide trench fill layer formed employing a sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method, where there is attenuated a surface sensitivity when forming the gap filling silicon oxide trench fill layer and where there is provided the gap filling silicon oxide trench fill layer with enhanced bulk properties (as determined through etch rate in dilute hydrofluoric acid) and with diminished surface roughness. The method of the present invention realizes these objects by forming, while employing a thermal oxidation method, within a trench within a silicon substrate a thermal silicon oxide trench liner layer and subsequently plasma treating the thermal silicon oxide trench liner layer to form a plasma treated thermal silicon oxide trench liner layer prior to forming upon the plasma treated thermal silicon oxide trench liner layer a conformal silicon oxide intermediate layer formed employing a plasma enhanced chemical vapor deposition (PECVD) method. There is then formed upon the conformal silicon oxide intermediate layer the gap filling silicon oxide trench fill layer formed employing the ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method.

The method of the present invention may be employed where the substrate is a semiconductor substrate and where the trench is an isolation trench within the semiconductor substrate. Provided that the substrate is a silicon substrate, the method of the present invention does not discriminate with respect to the nature of the trench which is formed within the substrate. Thus, the method of the present invention may be employed where the substrate is a semiconductor substrate and the trench is an isolation trench within the semiconductor substrate.

The method of the present invention is readily commercially implemented. The method of the present invention provides a novel ordering of integrated circuit thermal oxidation methods, nitrogen containing species and oxygen containing species plasma treatment methods and silicon oxide layer deposition methods which are otherwise generally known in the art of integrated circuit fabrication. Thus, the method of the present invention is readily commercially implemented.

BRIEF DESCRIPTION OF THE DRAWINGS

The objects, features and advantages of the present invention are understood within the context of the Description of the Preferred Embodiment, as set forth below. The Description of the Preferred Embodiment is understood within the context of the accompanying drawings, which form a material part of this disclosure, wherein:

FIG. 1, FIG. 2, FIG. 3, FIG. 4, FIG. 5, and FIG. 6 show a series of schematic cross-sectional diagrams illustrating the results of progressive stages in forming within an isolation trench within a silicon semiconductor substrate employed in integrated circuit fabrication a patterned planarized gap filling silicon oxide trench fill layer formed, while attenuating a surface sensitivity and with enhanced bulk properties and diminished surface roughness, in accord with a preferred embodiment of the method of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENT

The present invention provides a method for forming, while attenuating a surface sensitivity and while providing enhanced bulk properties and a diminished surface roughness, a gap filling silicon oxide trench fill layer formed employing an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method within a trench within a silicon substrate employed within microelectronics fabrication. To achieve the foregoing objects, the method of the present invention provides that there is formed within the trench within the silicon substrate through a thermal oxidation method a thermal silicon oxide trench liner layer. There is then plasma treated the thermal silicon oxide trench liner layer to form a plasma treated thermal silicon oxide trench liner layer surface. There is then formed upon the plasma treated thermal silicon oxide trench liner layer a conformal silicon oxide intermediate layer formed employing a plasma enhanced chemical vapor deposition (PECVD) method employing a silane silicon source material. There is finally formed upon the conformal silicon oxide intermediate layer a gap filling silicon oxide trench fill layer formed employing an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employing an ozone oxidant and a tetra-ethyl-ortho-silicate (TEOS) silicon source material.

Although the preferred embodiment of the method of the present invention illustrates the method of the present invention employed in forming, while attenuating a surface sensitivity and while providing enhanced bulk properties and a diminished surface roughness, a pair of patterned planarized gap filling silicon oxide trench fill layers within a pair of isolation trenches within a silicon semiconductor substrate employed in integrated circuit fabrication, the method of the present invention may also be employed in forming, while attenuating a surface sensitivity and while providing enhanced bulk properties and a diminished surface roughness, a gap filling silicon oxide trench fill layer or a patterned planarized gap filling silicon oxide trench fill layers of the method of the present invention within trenches other than isolation trenches within silicon substrates other than silicon semiconductor substrates. The method of the present invention may be employed in forming, while attenuating a surface sensitivity and while providing enhanced bulk properties and a diminished surface roughness, a gap filling silicon oxide silicon trench fill layer or a patterned planarized gap filling silicon oxide trench fill layer of the present invention into a trench within a silicon substrate including but not limited to a silicon semiconductor substrate and a silicon solar cell substrate. For a general embodiment of the method of the present invention, the width of the trench into which is formed the gap filling silicon oxide trench fill layer is preferably greater than about 0.3 microns and the depth of the trench is preferably from about 3000 to about 5000 angstroms.

Referring now to FIG. 1 to FIG. 6, there is shown a series of schematic cross-sectional diagrams illustrating the results of progressive stages in forming, while attenuating a surface sensitivity and while providing enhanced bulk properties and a diminished surface roughness, a pair of patterned planarized gap filling silicon oxide trench fill layers within a pair of isolation trenches within a silicon semiconductor substrate in accord with a preferred embodiment of the method of the present invention. Shown in FIG. 1 is a schematic cross-sectional diagram of the silicon semiconductor substrate at an early stage in its fabrication.

Shown in FIG. 1 is a silicon semiconductor substrate 10 having formed therein a pair of isolation trenches 11a and 11b, where a gap filling silicon oxide trench fill dielectric layer when formed into the pair of isolation trenches 11a and 11b employing a sub-atmospheric pressure chemical vapor deposition (SACVD) method conventional in the art of integrated circuit fabrication is typically formed with an enhanced surface sensitivity, an inferior bulk quality and an enhanced surface roughness. Although the method of the present invention may be practiced employing silicon semiconductor substrates of either doped polarity, any dopant concentration and various crystallographic orientations, within the preferred embodiment of the method of the present invention the silicon semiconductor substrate 10 is preferably a (100) silicon semiconductor substrate having an N- or P- doping.

As is illustrated in FIG. 1, each of the isolation trenches 11a and 11b within the silicon semiconductor substrate 10 has a width W1 and a height H1, where the width W1 is preferably greater than about 0.3 microns and the height H1 is preferably from about 3000 to about 5000 angstroms.

Formed upon the silicon semiconductor substrate 10 and defining the widths W1 of the isolation trenches 11a and 11b is a series of patterned silicon oxide pad oxide layers 12a, 12b and 12c having formed and aligned thereupon a series of patterned silicon nitride layers 14a, 14b and 14c. Within the preferred embodiment of the method of the present invention, the series of patterned silicon nitride layers 14a, 14b and 14c serves as a series of patterned chemical mechanical polish (CMP) polish stop layers, while the series of patterned silicon oxide pad oxide layers 12a, 12b and 12c serves as a series of adhesive forming and stress reducing layers between the silicon semiconductor substrate 10 and the series of patterned silicon nitride layers 14a, 14b and 14c. While the series of patterned silicon oxide pad oxide layers 12a, 12b and 12c, and the series of patterned silicon nitride layers 14a, 14b and 14c are preferably employed within the preferred embodiment of the method of the present invention, they are not required within the method of the present invention. However, their presence provides a means for most uniformly forming within the isolation trenches 11a and 11b patterned planarized gap filling silicon oxide trench fill layers through the preferred embodiment of the method of the present invention.

The patterned silicon oxide pad oxide layers 12a, 12b and 12c, and the patterned silicon nitride layers 14a, 14b and 14c may be formed employing methods as are conventional in the art of integrated circuit fabrication, which methods will typically, although not exclusively, employ photolithographic patterning of a blanket silicon oxide pad oxide layer which is formed beneath a corresponding blanket silicon nitride layer. The blanket silicon nitride layer and the blanket silicon oxide pad oxide layer may be similarly be formed employing methods as are conventional in the art of integrated circuit fabrication, including but not limited to thermal oxidation methods, chemical vapor deposition (CVD) methods, and the physical vapor deposition (PVD) sputtering methods, as are appropriate. Preferably, the patterned silicon oxide pad oxide layers 12a, 12b and 12c, and the corresponding blanket silicon oxide pad oxide layer, are formed to a thickness of from about 90 to about 130 angstroms each, where the blanket silicon oxide pad oxide layer is preferably formed employing a thermal oxidation method at a temperature of from about 850 to about 950 degrees centigrade. Preferably, the patterned silicon nitride layers 14a, 14b and 14c, and the corresponding blanket silicon nitride layer, are formed to a thickness of from about 1500 to about 2000 angstroms each.

Referring now to FIG. 2, there is shown a schematic cross-sectional diagram illustrating the results of further processing of the silicon semiconductor substrate 10 whose schematic cross-sectional diagram is illustrated in FIG. 1. Shown in FIG. 2 is the presence of a pair of patterned silicon oxide trench liner layers 12d and 12e formed into the corresponding isolation trenches 11a and 11b. Within the preferred embodiment of the method of the invention, the patterned silicon oxide trench liner layers 12d and 12e are formed in a self aligned fashion within each isolation trench 11a or 11b while employing a thermal oxidation method analogous or equivalent to the thermal oxidation method preferably employed in forming the blanket silicon oxide pad oxide layer from which is formed the patterned silicon oxide pad oxide layers 12a, 12b and 12c. Under such circumstances, there is simultaneously also formed from the silicon semiconductor substrate 10 a partially consumed silicon semiconductor substrate 10' when the patterned silicon oxide trench liner layers 12d and 12e are formed within the isolation trenches 11a and 11b. Preferably, the patterned silicon oxide trench liner layers 12d and 12e so formed have a thickness of from about 200 to about 400 angstroms each. The patterned silicon oxide trench liner layers 12d and 12e are particularly desirable within advanced integrated circuit fabrication since, when formed employing a thermal oxidation method, they provide a superior leakage barrier between the partially consumed silicon semiconductor substrate 10' and trench fill dielectric layers subsequently formed within the isolation trenches 11a and 11b. Unfortunately, when formed through the thermal oxidation method, the patterned silicon oxide trench liner layers 12d and 12e provide substrate layers upon which there is exhibited a surface sensitivity manifested as an inhibited formation rate of gap filling silicon oxide trench fill layers formed employing conventional ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods upon the patterned silicon oxide trench liner layers 12d and 12e. Such gap filling silicon oxide trench fill layers so formed typically also exhibit inferior bulk quality (as determined through etch rates in dilute hydrofluoric acid) and enhanced surface roughness.

Referring now to FIG. 3, there is shown a schematic cross-sectional diagram illustrating the results of further processing of the partially consumed silicon semiconductor substrate whose schematic cross-sectional diagram is illustrated in FIG. 2. Shown in FIG. 3 is a schematic cross-sectional diagram of a partially consumed silicon semiconductor substrate 10' otherwise equivalent to the partially consumed silicon semiconductor substrate whose schematic cross-sectional diagram is illustrated in FIG. 2, but wherein there is treated the patterned silicon oxide trench liner layers 12d and 12e with a plasma 16 to form a pair of plasma treated patterned silicon oxide trench liner layers 12d' and 12e'. Within the method of the present invention, the plasma 16 employs a plasma gas composition which upon plasma activation simultaneously provides active nitrogen-containing species plus active oxygen-containing species. Preferably, the plasma gas composition comprises nitrous oxide (N2O) although other nitrogen and oxygen containing gases, or mixtures of nitrogen and oxygen containing plasma gases may also be employed. Such other nitrogen and oxygen containing plasma gases may include, but are not limited to, nitric oxide (NO) and dinitrogen tetroxide (N2O4). Such mixtures may include molecular nitrogen (N2), molecular oxygen (O2) and ozone (O3) with effective amounts of nitrous oxide (N2O), nitric oxide (NO) and dinitrogen tetroxide (N2O4).

The plasma also preferably employs when processing an 8-inch diameter partially consumed silicon semiconductor substrate: (1) a reactor chamber pressure of from about 1 to about 2 torr; (2) a first radio frequency power of from about 50 to about 150 watts at a first radio frequency of 13.56 MHz and a simultaneous second radio frequency power of from about 400 to about 550 watts at a simultaneous second radio frequency of 550 kHz; (3) a partially consumed silicon semiconductor substrate 10' temperature of from about 360 to about 440 degrees centigrade; (4) a nitrous oxide (N2O) flow rate of from about 400 to about 600 standard cubic centimeters per minute (sccm); and (5) a background helium gas flow rate of from about 1500 to about 2500 standard cubic centimeters per minute (sccm). Preferably, the plasma treated patterned silicon oxide trench liner layers 12d' and 12e' are formed from the patterned silicon oxide trench liner layers 12d and 12e by exposure of the patterned silicon oxide trench liner layers 12d and 12e to the plasma 16 for a time period of from about 50 to about 70 seconds.

Referring now to FIG. 4, there is shown a schematic cross-sectional diagram illustrating the results of further processing of the partially consumed silicon semiconductor substrate 10' whose schematic cross-sectional diagram is shown in FIG. 3. Shown in FIG. 4 is a schematic cross-sectional diagram of the partially consumed silicon semiconductor substrate 10' shown in FIG. 3, but wherein there is formed over the partially consumed silicon semiconductor substrate 10' and upon the plasma treated patterned thermal silicon oxide trench liner layers 12d' and 12e' a conformal silicon oxide intermediate layer 18. For the method of the present invention, the conformal silicon oxide intermediate layer 18 is formed employing a plasma enhanced chemical vapor deposition (PECVD) method employing a silane silicon source material. Preferably, the plasma enhanced chemical vapor deposition (PECVD) method through which is formed the conformal silicon oxide intermediate layer 18 also employs: (1) a reactor chamber pressure of from about 2.5 to about 3.5 torr; (2) a radio frequency power of from about 150 to about 250 watts at a frequency of 13.56 MHz; (3) a partially consumed silicon semiconductor substrate 10' temperature of from about 360 to about 440 degrees centigrade; (4) a silane gas flow rate of from about 60 to about 100 standard cubic centimeters per minute (sccm); and (5) a nitrous oxide (N2O) gas oxidant flow rate of from about 1500 to about 2000 standard cubic centimeters per minute (sccm). Preferably, the conformal silicon oxide intermediate layer 18 is formed to a thickness of from about 300 to about 500 angstroms over the partially consumed silicon semiconductor substrate 10' and upon the plasma treated patterned silicon oxide trench liner layers 12d' and 12e'.

Referring now to FIG. 5, there is shown a schematic cross-sectional diagram illustrating the results of further processing of the partially consumed silicon semiconductor substrate 10' whose schematic cross-sectional diagram is illustrated in FIG. 4. Shown in FIG. 5 is a schematic cross-sectional diagram of a partially consumed silicon semiconductor substrate 10' otherwise equivalent to the partially consumed silicon semiconductor substrate 10' whose schematic cross-sectional diagram is illustrated in FIG. 4, but wherein there is formed upon the conformal silicon oxide intermediate layer 18 a gap filling silicon oxide trench fill layer 20. Within the method of the present invention, the gap filling silicon oxide trench fill layer 20 is formed through an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method. Due to the elevated pressures at which ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) methods are employed, these methods preclude plasma activation, but nonetheless provide superior gap filling and planarizing properties to gap filling silicon oxide silicon oxide trench fill layers formed employing these methods. Preferably, the ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employed in forming the gap filling silicon oxide trench fill layer 20 employs an ozone gas oxidant and a tetra-ethyl-ortho-silicate (TEOS) silicon source material at an ozone:TEOS volume ratio of from about 10:1 to about 15:1.

Other parameters employed in forming the gap filling silicon oxide trench fill layer 20 while employing the sub-atmospheric pressure chemical vapor deposition (SACVD) method include: (1) a reactor chamber pressure of from about 400 to about 600 torr; (2) a partially consumed silicon semiconductor substrate 10' temperature of from about 360 to about 440 degrees centigrade; (3) an ozone gas concentration of about 10 to about 14 weight percent in an oxygen carrier gas; (4) a tetra-ethyl-ortho-silicate (TEOS) vapor flow rate of from about 27 to about 42 standard cubic centimeters per minute (sccm); (5) an oxygen (ozone carrier gas) flow rate of from about 4000 to about 6000 standard cubic centimeters per minute (sccm); and (6) a helium (tetra-ethyl-ortho-silicate (TEOS) vapor carrier gas) flow rate of from about 1850 to about 2750 standard cubic centimeters per minute (sccm). Preferably, the gap filling silicon oxide trench fill layer 20 is formed to a thickness of from about 6000 to about 8000 angstroms over the partially consumed silicon semiconductor substrate 10' and upon the conformal silicon oxide intermediate layer 18.

As illustrated in FIG. 5, the gap filling silicon oxide trench fill layer 20 is formed while avoiding a surface sensitivity over the isolation trenches 11a and 11b since within the preferred embodiment of the method of the present invention the gap filling silicon oxide trench fill layer 20 is formed upon the conformal silicon oxide intermediate layer 18 which in turn is formed upon the pair of plasma treated patterned silicon oxide trench liner layers 12d' and 12e' rather than upon the pair of patterned silicon oxide trench liner layers 12d and 12e. While within the method of the present invention a conformal silicon oxide intermediate layer, such as the conformal silicon oxide intermediate layer 18, may by itself provide an intermediate layer upon which may be formed a gap filling silicon oxide trench fill layer, such as the gap filling silicon oxide trench fill layer 20, while attenuating a surface sensitivity over a pair of patterned silicon oxide trench fill layers, such as the pair of patterned silicon oxide trench liner layers 12d and 12e, without treating the patterned silicon oxide trench liner layers with a plasma, within the preferred embodiment of the method of the present invention the conformal silicon oxide intermediate layer 18 is typically too thin to totally attenuate the surface sensitivity of the gap filling silicon oxide trench fill layer 20 with respect to the patterned silicon oxide trench liner layers 12d and 12e while still optimizing the gap filling characteristics of the gap filling silicon oxide trench fill layer 20.

Referring now to FIG. 6, there is shown a schematic cross-sectional diagram illustrating the results of further processing of the partially consumed silicon semiconductor substrate 10' whose schematic cross-sectional diagram is illustrated in FIG. 5. Shown in FIG. 6 is the results of planarizing, through a chemical mechanical polish (CMP) planarizing method, the gap filling silicon oxide trench fill layer 20 and the conformal silicon oxide intermediate layer 18 as illustrated in FIG. 5 to form the patterned planarized conformal silicon oxide intermediate layers 18a and 18b having formed thereupon the patterned planarized gap filling silicon oxide trench fill layers 20a and 20b.

While any of several parameters may be employed within the chemical mechanical polish (CMP) planarizing method for forming from the gap filling silicon oxide trench fill layer 20 and the conformal silicon oxide intermediate layer 18 the patterned planarized conformal silicon oxide intermediate layers 18a and 18b and the patterned planarized gap filling silicon oxide trench fill layers 20a and 20b, the chemical mechanical polish (CMP) planarizing method employed within the preferred embodiment of the method of the present invention preferably employs: (1) a platen pressure of from about 5 to about 10 pounds per square inch (psi); (2) a platen rotation speed of from about 30 to about 60 revolutions per minute (rpm); (3) a holder counter-rotation speed of from about 30 to about 60 revolutions per minute (rpm); and (4) an aqueous silica slurry comprising about 10 to about 20 weight percent silica at a flow rate of from about 100 to about 250 cubic centimeters per minute.

EXAMPLES 1-8

Upon each silicon semiconductor substrate within a series of eight silicon semiconductor substrates each 8 inches in diameter there was formed a thermal silicon oxide layer employing thermal oxidation of the silicon semiconductor substrate at a temperature of about 900 degrees centigrade for a time period of about 60 minutes. Each of the thermal silicon oxide layers so formed was formed to a thickness of about 350 angstroms.

The thermal silicon oxide layer formed upon a first of the eight silicon semiconductor substrates was given no further treatment prior to deposition of silicon oxide.

The thermal silicon oxide layer formed upon a second of the eight silicon semiconductor substrates was exposed to a nitrogen plasma. The nitrogen plasma employed: (1) a reactor chamber pressure of about 1.5 torr; (2) a first radio frequency power of about 100 watts at a first radio frequency of 13.56 MHz and a simultaneous second radio frequency power of about 450 watts at a simultaneous second radio frequency of 350 kHz; (3) a silicon semiconductor substrate temperature of about 400 degrees centigrade; (4) a nitrogen gas flow rate of about 500 standard cubic centimeters per minute (sccm); and (5) a background helium gas flow rate of about 2000 standard cubic centimeters per minute (sccm). The thermal silicon oxide layer formed on the silicon semiconductor substrate was treated with the nitrogen plasma for a time period of about 60 seconds.

Upon the thermal silicon oxide layer formed upon a third of the eight silicon semiconductor substrates was formed a second silicon oxide layer formed by a low ozone (O3) method. The low ozone method of silicon oxide deposition employed: (1) a reactor chamber pressure of about 60 torr; (2) a silicon semiconductor substrate temperature of about 400 degrees centigrade; (3) an oxygen (ozone carrier gas) gas flow rate of about 4000 standard cubic centimeters per minute (sccm); (4) a tetra-ethyl-ortho-silicate (TEOS) silicon source gas flow rate of about 250 standard cubic centimeters per minute (sccm); (5) a helium (TEOS carrier gas) gas flow rate of about 1200 standard cubic centimeters per minute (sccm); and (6) an ozone concentration in oxygen carrier gas of about 8 percent by weight.

Upon the thermal silicon oxide layer formed upon a fourth of the eight silicon semiconductor substrates there was formed a second silicon oxide layer through the use of plasma enhanced chemical vapor deposition (PECVD) method employing silage (SiH4) gas as a silicon source material. The method employed: (1) a reactor chamber pressure of about 2.8 torr; (2) a radio frequency power of about 200 watts at a radio frequency of 13.56 MHz; (3) a silicon semiconductor substrate temperature of about 400 degrees centigrade; (4) a silane vapor flow rate of about 80 standard cubic centimeters per minute (sccm); and (5) a nitrous oxide gas oxidant flow rate of about 180 standard cubic centimeters per minute (sccm). The second silicon oxide layer so formed upon the fourth silicon semiconductor substrate was formed to a thickness of about 500 angstroms.

Upon the thermal oxide layer formed upon a fifth of the eight silicon semiconductor substrates was formed a second silicon oxide layer in accord with the second silicon layer formed on the fourth of the eight silicon semiconductor substrates but where the second silicon oxide layer deposition was preceded by exposure of the thermal silicon oxide layer to a nitrogen plasma treatment in accord with the nitrogen plasma treatment of the second of the nine silicon semiconductor substrates.

Upon the thermal silicon oxide layer formed upon a sixth of the eight semiconductor substrates there was formed a second silicon oxide layer through the use of a plasma enhanced chemical vapor deposition (PECVD) method employing tetra-ethyl-ortho-silicate (TEOS) vapor as the silicon source material, but wherein the deposition of the second layer of silicon oxide was preceded by exposure of the thermal silicon oxide layer to a nitrogen plasma in accord with the second of the eight silicon semiconductor substrates. The plasma enhanced chemical vapor deposition (PECVD) method employed: (1) a reactor chamber pressure of about 8 torr; (2) a radio frequency source of about 675 watts at a radio frequency of 13.56 MHz; (3) a silicon semiconductor substrate temperature of about 400 degrees centigrade; and (4) a TEOS vapor in helium carrier gas flow rate of about 150 standard cubic centimeters per minute (sccm). The second silicon oxide layer so formed upon the thermal silicon oxide of the sixth of the eight silicon semiconductor substrate was formed to a thickness of about 500 angstroms.

Upon the thermal silicon oxide formed upon a seventh of the eight silicon semiconductor substrates was formed a second silicon layer in accord with the second silicon oxide layer formed upon the fourth of the eight silicon semiconductor substrates but where the deposition of the second silicon oxide layer was preceded by exposure of the thermal silicon oxide layer to a nitrogen plasma in accord with the nitrogen plasma treatment of the second of the eight silicon semiconductor substrates.

Upon the thermal silicon oxide layer formed upon an eighth of the eight silicon semiconductor substrates was deposited a second silicon oxide layer in accord with the second layer formed on the fourth of the eight silicon semiconductor substrates but where the deposition of the second silicon oxide layer was preceded by treatment of the thermal silicon oxide layer to a plasma containing simultaneously active nitrogen containing species and active oxygen containing species in accord with the method of the present invention. The plasma employed: (1) a reactor chamber pressure of about 2.8 torr; (2) a radio frequency power of about 200 watts at a radio frequency of 13.56 MHz; (3) a silicon semiconductor substrate temperature of about 400 degrees centigrade; (4) a nitrous oxide gas flow rate of about 500 standard cubic centimeters per minute (sccm). The thermal silicon oxide layer was treated to the plasma for a time period of about 60 seconds.

There was formed upon all eight silicon semiconductor wafers after treatment as described a gap filling silicon oxide layer formed employing an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employing an ozone oxidant and a tetra-ethyl-ortho-silicate (TEOS) silicon source material. The ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method also employed: (1) a reactor chamber pressure of about 450 torr; (2) a silicon semiconductor substrate temperature of about 400 degrees centigrade; (3) an ozone:TEOS volume ratio of about 12:1; (4) an ozone concentration in oxygen (ozone carrier gas) of from about 10 to about 14 weight percent; (5) a tetra-ethyl-ortho-silicate (TEOS) vapor flow rate of about 35 standard cubic centimeters per minute (sccm); (6) an oxygen flow rate of about 5000 standard cubic centimeters per minute (sccm); and (7) a helium (tetra-ethyl-ortho-silicate (TEOS) carrier gas) flow rate of about 2000 standard cubic centimeters per minute (sccm).

There was determined employing ellipsometric measurements the deposition rates for the eight gap filling silicon oxide layers upon the eight silicon substrates designated in Examples 1 through 8. In addition, there was also determined the etch rate of each of the eight gap filling silicon oxide layers designated in Examples 1 through 8 in 50:1 dilute hydrofluoric acid solution. The etch rates so determined were then normalized to the etch rate of a thermal silicon oxide layer within the same 50:1 dilute hydrofluoric acid solution. Finally, there was also determined for each of the eight gap filling silicon oxide layers designated in Examples 1 through 8 surface roughness employing a scanning electron microscopy inspection. The values of the deposition rates, the normalized 50:1 dilute hydrofluoric acid etch rates and the surface roughness for the eight gap filling silicon oxide layers on the eight silicon semiconductor substrates designated in Examples 1 through 8 are reported in Table 1.

                  TABLE 1                                                          ______________________________________                                                                         Wet                                                                  Deposition                                                                               Etch                                                                 Rate      Rate   Rough-                                  Ex-   Thermal Silicon (angstroms/                                                                              (normal-                                                                              ness                                    ample Oxide Substrate Layer                                                                          min)      ized)  (SEM)                                   ______________________________________                                         1     --              0.10      --     rough                                   2     N2 Plasma       0.93      1.08   rough                                   3     Low O3 Ox       1.00      1.03   smooth                                  4     PECVD SiH4      1.00      1.01   smooth                                  5     PECVD SiH4/N2 Plasma                                                                           0.89      1.08   rough                                   6     PE-TEOS/N2 Plasma                                                                              0.84      1.09   rough                                   7     N2 Plasma/PECVD SiH4                                                                           1.01      1.00   smooth                                  8     N2O Plasma/PECVD SiH4                                                                          1.02      0.98   smooth                                  ______________________________________                                    

As is seen from the data in Table 1, a silicon oxide layer formed employing a thermal oxidation method, and having a second silicon oxide layer thereupon formed employing a plasma enhanced chemical vapor deposition (PECVD) method employing a silane source material, provides a substrate layer upon which there is formed a gap filling silicon oxide layer through an ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method while attenuating a surface sensitivity when forming the gap filling silicon oxide layer and while providing a gap filling silicon oxide layer with enhanced bulk properties and with diminished surface roughness.

As is understood by a person skilled in the art, the preferred embodiment and examples of the present invention are illustrative of the present invention rather than limiting of the present invention. Revisions and modifications may be made to materials, structures and dimensions through which is provided the preferred embodiment and examples of the present invention while still providing embodiments and examples which are within the spirit and scope of the present invention, as defined by the appended claims. 

What is claimed is:
 1. A method for filling a trench within a silicon substrate comprising:providing a silicon substrate, the silicon substrate having a trench formed therein; oxidizing thermally the silicon substrate to form within the trench a thermal silicon oxide trench liner layer; treating the thermal silicon oxide trench liner layer with a plasma formed from a plasma gas phase composition which upon plasma activation simultaneously supplies active nitrogen containing species and active oxygen containing species to form a plasma treated thermal silicon oxide trench liner layer, wherein the plasma gas composition is nitrous oxide and the plasma is employed at:a reactor chamber pressure of from about 1 to about 2 torr; a radio frequency power of about 50 to about 150 watts at a radio frequency of 13.56 MHz; a nitrous oxide gas flow of from about 400 to about 600 standard cubic centimeters per minute (sccm); forming upon the thermal silicon oxide trench liner layer a conformal silicon oxide intermediate layer formed through a plasma enhanced chemical vapor deposition (PECVD) method employing silane as a silicon source material; and forming upon the conformal silicon oxide intermediate layer a gap filling silicon oxide trench fill layer formed employing a sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employing ozone as an oxidant and tetra-ethyl-ortho-silicate (TEOS) as a silicon source material.
 2. The method of claim 1 wherein the plasma treatment of the thermal silicon oxide trench liner layer provides the gap filling silicon oxide trench fill layer with attenuated surface sensitivity, enhanced bulk properties and attenuated surface roughness.
 3. The method of claim 1 wherein:the silicon substrate is a silicon semiconductor substrate; and the trench is an isolation trench within the silicon semiconductor substrate.
 4. The method of claim 1 wherein the width of the trench is greater than about 0.3 microns and the depth of the trench is from about 3000 to about 5000 angstroms.
 5. The method of claim 1 wherein:the thermal silicon oxide trench liner layer is formed to a thickness of from about 200 to about 400 angstroms; and the conformal silicon oxide intermediate layer is formed to a thickness greater than about 300 angstroms.
 6. The method of claim 1 wherein the plasma gas composition is selected from the group consisting of nitrous oxide, nitric oxide, dinitrogen tetroxide, nitrogen and oxygen mixtures and mixtures thereof.
 7. The method of claim 1 wherein the ozone assisted sub-atmospheric pressure thermal chemical vapor deposition (SACVD) method employs a reactor chamber pressure of from about 400 to about 600 torr and an ozone:tetra-ethyl-ortho-silicate volume ratio of from about 10:1 to about 15:1.
 8. The method of claim 1 further comprising planarizing the gap filling silicon oxide trench fill layer to form within the trench a planarized gap filling silicon oxide trench fill layer. 